- 密度 [g/cm3]: 1.67
- 缺口冲击强度: 0.8
- 弯曲模量 [MPa]: 13.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 2.00 mm | 0.0050 in/in @Thickness 0.0787 in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | ASTM D955 |
| Ash | 45 % | 45 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 240 MPa | 34800 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C | 1.50 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 275 °C | 518 - 527 °F | |
| Front Barrel Temperature | 275 - 280 °C | 527 - 536 °F | |
| Nozzle Temperature | 275 - 290 °C | 527 - 554 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | |
| Mold Temperature | 75.0 - 100 °C | 167 - 212 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi | |