- 密度 [g/cm3]: 1.79
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.74
- 断裂伸长率 [%]: 180
- 弯曲强度 [MPa]: 105.9
- 弯曲模量 [MPa]: 10.38
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 105.9 MPa | 15360 psi | ASTM D638 |
| Elongation at Break | 1.18 % | 1.18 % | ASTM D638 |
| Tensile Modulus | 13.2 GPa | 1910 ksi | ASTM D638 |
| Flexural Yield Strength | 180 MPa | 26100 psi | ASTM D790 |
| Flexural Modulus | 10.38 GPa | 1506 ksi | ASTM D790 |
| Compressive Yield Strength | 164 MPa | 23800 psi | ASTM D695 |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.40e+16 ohm-cm | 2.40e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz | 3.7 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.013 @Frequency 1e+6 Hz | 0.013 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 20 sec | 20 sec | ASTM D495 |
| Comparative Tracking Index | 225 V | 225 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 219 °C | 426 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | |