- 缺口冲击强度: 0.2
- 拉伸强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 3.09
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.55 GPa | 370 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | At break, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.09 GPa | 448 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.200 J/cm @Temperature 23.0 °C | 0.375 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | 31000 ohm | 31000 ohm | ASTM D257 |