- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 0.23
- 热变形温度 [℃]: 67.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | |||
| Thickness | 406 microns | 16.0 mil | |||
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm | 0.0040 - 0.0060 in/in @Thickness 0.157 in | 10.0 mm wide molded rod; ISO 294-4 | ||
| Melt Flow | 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C | 5.0 g/10 min @Load 11.0 lb, Temperature 392 °F | ISO 1133 | ||
| High Load Melt Index | 35 g/10 min @Load 21.6 kg, Temperature 200 °C | 35 g/10 min @Load 47.6 lb, Temperature 392 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 99 @Thickness 4.00 mm | 99 @Thickness 0.157 in | 10.0 mm wide molded rod; ISO 868 | ||
| Film Tensile Strength at Yield, MD | 40.0 MPa | 5800 psi | ISO 527 | ||
| Film Tensile Strength at Yield, TD | 30.0 MPa | 4350 psi | ISO 527 | ||
| Film Elongation at Break, MD | 350 % | 350 % | ISO 527 | ||
| Film Elongation at Break, TD | 300 % | 300 % | ISO 527 | ||
| Film Elongation at Yield, MD | 5.0 % | 5.0 % | ISO 527 | ||
| Film Elongation at Yield, TD | 4.0 % | 4.0 % | ISO 527 | ||
| Modulus of Elasticity | 1.65 GPa @Thickness 4.00 mm | 239 ksi @Thickness 0.157 in | 10.0 mm wide molded rod; ISO 178 | ||
| Izod Impact, Notched | 0.230 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 0.431 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | ISO 180 | ||
| Izod Impact, Unnotched | NB @Thickness 4.00 mm, Temperature 23.0 °C | NB @Thickness 0.157 in, Temperature 73.4 °F | ISO 180 | ||
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527 | ||
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527 | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | <= 1.00e+10 ohm | <= 1.00e+10 ohm | 400 um thick sheet; ISO IEC 61340-5-1 | ||
| Static Decay | <= 1.0 sec | <= 1.0 sec | 400 um thick sheet; ISO IEC 61340-5-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C @Thickness 4.00 mm | 153 °F @Thickness 0.157 in | 10.0 mm wide molded rod; ISO 75/Method Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 4.00 mm | 140 °F @Thickness 0.157 in | 10.0 mm wide molded rod; ISO 75/Method Af | ||
| Vicat Softening Point | 72.0 °C @Thickness 4.00 mm | 162 °F @Thickness 0.157 in | Rate A; 10.0 mm wide molded rod; ISO 306/B50 | ||
| 82.0 °C @Thickness 4.00 mm | 180 °F @Thickness 0.157 in | Rate A; 10.0 mm wide molded rod; ISO 306/A50 | |||
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | ISO RD524 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ISO RD524 | |||
| Processing Properties | Metric | English | Comments | ||
| Middle Barrel Temperature | 190 °C | 374 °F | Zone 2; Cylinder | ||
| 190 °C | 374 °F | Zone 1; Cylinder | |||
| 200 °C | 392 °F | Zone 6; Cylinder | |||
| 200 °C | 392 °F | Zone 4; Cylinder | |||
| 200 °C | 392 °F | Zone 5; Cylinder | |||
| 200 °C | 392 °F | Zone 3; Cylinder | |||
| Die Temperature | 179 °C | 355 °F | Zone 3 | ||
| 188 °C | 370 °F | Zone 4 | |||
| 188 °C | 370 °F | Zone 1 | |||
| 188 °C | 370 °F | Zone 2 | |||
| 188 °C | 370 °F | Zone 5 | |||
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |||
| Mold Temperature | 30.0 - 70.0 °C | 86.0 - 158 °F | |||
| Roll Temperature | 30.0 °C | 86.0 °F | 3rd Roll | ||
| 40.0 °C | 104 °F | 2nd Roll | |||
| 50.0 °C | 122 °F | 1st Roll | |||
| Dry Time | 3 - 4 hour | 3 - 4 hour | No higher than 70°C; Pre-drying in a dehumidifier | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | When Produced | ||
| Injection Pressure | 75.2 - 120 MPa | 10900 - 17400 psi | |||
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions | ||
| Descriptive Properties | |||||
| Appearance | Granule | ||||
| Color | Whitish | ||||
| Injection Speed | Moderate | ||||
| Post Pressure, psi | 5800 - 8700 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.