- 熔体流动速率 [g/10min]: 36.0
- 密度 [g/cm3]: 1.49
- 缺口冲击强度: 0.27
- 拉伸强度 [MPa]: 45.0
- 断裂伸长率 [%]: 93.0
- 弯曲模量 [MPa]: 4.68
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Melt Flow | 36 g/10 min @Load 1.20 kg, Temperature 266 °C | 36 g/10 min @Load 2.65 lb, Temperature 511 °F | ASTM D1238 |
| 64 g/10 min @Load 2.16 kg, Temperature 265 °C | 64 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 | |
| Melt Index of Compound | 52 g/10 min @Load 2.16 kg, Temperature 265 °C | 52 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
| 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.80 GPa | 696 ksi | 1 mm/min; ISO 527 |
| 5.88 GPa | 853 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.68 GPa | 679 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.71 GPa | 683 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 70.0 °C @Thickness 3.20 mm | 158 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 179 °C | 354 °F | Rate B/120; ISO 306 |