SABIC Innovative Plastics LNP STAT-LOY 63000CT PC+POLYESTER (Asia Pacific)物性表参数

熔体流动速率 [g/10min]: 16.0
密度 [g/cm3]: 1.16
缺口冲击强度: 5.8
拉伸强度 [MPa]: 34.0
弯曲模量 [MPa]: 1.14
热变形温度 [℃]: 83.0
透光率 [%]: 81.0

Physical Properties	Metric	English	Comments

Density	1.16 g/cc	0.0419 lb/in³	ASTM D792
Moisture Absorption	0.700 %	0.700 %	23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0060 cm/cm	0.0060 in/in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	SABIC Method
Melt Flow	16 g/10 min @Load 2.16 kg, Temperature 260 °C	16 g/10 min @Load 4.76 lb, Temperature 500 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	34.0 MPa	4930 psi	5 mm/min; ISO 527
	35.0 MPa	5080 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	140 %	140 %	5 mm/min; ISO 527
	200 %	200 %	Type I, 10 mm/min; SABIC - Japan Method
Tensile Modulus	1.16 GPa	168 ksi	50 mm/min; ASTM D638
	1.18 GPa	171 ksi	1 mm/min; ISO 527
Flexural Strength	50.0 MPa	7250 psi	brk, 1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	1.14 GPa	165 ksi	2 mm/min; ISO 178
	1.16 GPa	168 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	5.80 J/cm	10.9 ft-lb/in	ASTM D256
Charpy Impact, Notched	6.90 J/cm²	32.8 ft-lb/in²	ISO 179/2C

Electrical Properties	Metric	English	Comments
Volume Resistivity	12 ohm-cm	12 ohm-cm	ASTM D257
Surface Resistance	12 ohm	12 ohm	ASTM D257
Static Decay	2.0 sec	2.0 sec	5000V to <50V; FTMS101B

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	83.0 °C @Thickness 6.40 mm	181 °F @Thickness 0.252 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	68.0 °C	154 °F	Flatw 80104 sp=64mm; ISO 75/Af
	73.0 °C @Thickness 6.40 mm	163 °F @Thickness 0.252 in	unannealed; ASTM D648

Optical Properties	Metric	English	Comments
Haze	10 % @Thickness 2.54 mm	10 % @Thickness 0.100 in	ASTM D1003
Transmission, Visible	81 %	81 %	2.54 mm; ASTM D1003

关键词:
PET
供应
SABIC Innovative Plastics LNP STAT-LOY 63000CT PC+POLYESTER (Asia Pacific)