- 熔体流动速率 [g/10min]: 18.0
- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.8
- 拉伸强度 [MPa]: 100.0
- 断裂伸长率 [%]: 170
- 弯曲模量 [MPa]: 7.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH |
| 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 | |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ASTM D570 |
| 0.15 % | 0.15 % | ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 265 °C | 18 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Melt Index of Compound | 13 g/10 min @Load 2.16 kg, Temperature 260 °C | 13 g/10 min @Load 4.76 lb, Temperature 500 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 100 MPa | 14500 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.00 GPa | 1160 ksi | 5 mm/min; ASTM D638 |
| 9.00 GPa | 1310 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 170 MPa | 24700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 200 MPa | 29000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C | 1.31 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C | 5.16 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 13.9 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| 25.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 13.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 44.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 81.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 45.0 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 195 °C @Thickness 3.20 mm | 383 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 200 °C | 392 °F | Rate B/50; ISO 306 |
| 200 °C | 392 °F | Rate B/50; ASTM D1525 | |
| 205 °C | 401 °F | Rate B/120; ISO 306 | |