- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.37
- 缺口冲击强度: 8.54
- 拉伸强度 [MPa]: 57.0
- 断裂伸长率 [%]: 94.0
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 116.0
- 透光率 [%]: 88.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.130 % | 0.130 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.37 % | 0.37 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Melt Index of Compound | 3.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 92 % | 92 % | Type I, 50 mm/min; ASTM D638 |
| 117 % | 117 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.8 % | 5.8 % | 50 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.18 GPa | 316 ksi | 1 mm/min; ISO 527 |
| 2.37 GPa | 344 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 89.0 MPa | 12900 psi | break, 2 mm/min; ISO 178 |
| Flexural Yield Strength | 94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| 2.00 J/cm @Temperature -30.0 °C | 3.75 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -10.0 °C | 3.81 ft-lb/in² @Temperature 14.0 °F | 80*10*4; ISO 180/1A | |
| 8.00 kJ/m² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 70.0 J @Temperature 23.0 °C | 51.6 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 33.3 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| 104 µm/m-°C @Temperature -40.0 - 40.0 °C | 57.8 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| 104 µm/m-°C @Temperature -40.0 - 40.0 °C | 57.8 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 38.9 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| 104 µm/m-°C @Temperature -40.0 - 40.0 °C | 57.8 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| 104 µm/m-°C @Temperature -40.0 - 40.0 °C | 57.8 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C @Thickness 3.20 mm | 241 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 104 °C @Thickness 3.20 mm | 219 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 121 °C | 250 °F | Rate B/50; ISO 306 |
| 123 °C | 253 °F | Rate B/120; ISO 306 | |
| 123 °C | 253 °F | Rate B/50; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.576 | 1.576 | ASTM D542 |
| Haze | 1.5 % @Thickness 2.54 mm | 1.5 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |