- 密度 [g/cm3]: 1.29
- 弯曲模量 [MPa]: 2.35
- 热变形温度 [℃]: 69.0
- 透光率 [%]: 87.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527-2 |
| Elongation at Break | 14 % | 14 % | ISO 527-2 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527-2 |
| Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 |
| Flexural Modulus | 2.35 GPa | 341 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179-1 |
| Charpy Impact, Notched | 0.153 J/cm² | 0.728 ft-lb/in² | ISO 179-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.05e+14 ohm-cm | 6.05e+14 ohm-cm | IEC 93 |
| Surface Resistance | 6.62e+14 ohm | 6.62e+14 ohm | IEC 93 |
| Dielectric Constant | 3.3 @Frequency 1000 Hz | 3.3 @Frequency 1000 Hz | |
| Dielectric Strength | 10.7 kV/mm | 272 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 @Frequency 50 Hz | 0.020 @Frequency 50 Hz | IEC 250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 59.0 µm/m-°C @Temperature 20.0 °C | 32.8 µin/in-°F @Temperature 68.0 °F | DIN 53752 |
| Thermal Conductivity | 0.162 W/m-K | 1.12 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 69.0 °C | 156 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75-2 |
| Vicat Softening Point | 78.0 °C | 172 °F | ISO 306 |
| Decomposition Temperature | >= 280 °C | >= 536 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.1 % | <= 1.1 % | |
| Transmission, Visible | 87 % | 87 % | DIN 5036-3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 120 - 160 °C | 248 - 320 °F | Sheet Forming |
- 关键词:
- PET
- 供应
- Polycasa COPOL PETG