- 熔体流动速率 [g/10min]: 35.0
- 缺口冲击强度: 0.588
- 断裂伸长率 [%]: 47.9
- 弯曲强度 [MPa]: 42.2
- 弯曲模量 [MPa]: 0.8574
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 190 °C | 35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength, Ultimate | 42.2 MPa | 6120 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Yield Strength | 47.9 MPa | 6940 psi | ASTM D790 |
| Flexural Modulus | 0.8574 GPa | 124.4 ksi | ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 118 °C | 244 °F | ASTM D3418 |
| Softening Point | 97.0 °C | 207 °F | ASTM D1525 |