- 吸水率 [%]: 0.13
- 缺口冲击强度: 1.0
- 拉伸强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 2.10
- 硬度: 110.0
- 热变形温度 [℃]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Water Absorption | 0.13 % | 0.13 % | 24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 140 % | 140 % | 50mm/min; ASTM D638 |
| Flexural Strength | 73.0 MPa | 10600 psi | 1.27 mm/min; ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 1.27 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Impact Test | 33.0 J @Thickness 3.20 mm | 24.3 ft-lb @Thickness 0.126 in | impact resistance energy, max. load in plaque, 220 m/min; ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.4 @Frequency 1e+6 Hz | 2.4 @Frequency 1e+6 Hz | ASTM D150 |
| 2.6 @Frequency 1000 Hz | 2.6 @Frequency 1000 Hz | ASTM D150 | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | short-time, 500v/sec; ASTM D149 |
| Dissipation Factor | 0.0050 @Frequency 1000 Hz | 0.0050 @Frequency 1000 Hz | ASTM D150 |
| 0.023 @Frequency 1e+6 Hz | 0.023 @Frequency 1e+6 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Vicat Softening Point | 85.0 °C | 185 °F | at 1 kg load; ASTM D1525 |
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | DSC |
| Flammability, UL94 | HB | HB | min. 1.6 thickness |
| V-2 | V-2 | min. 3.2 thickness | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 45.0 °C | 113 °F | Roll 1 Temperature |
| 54.0 °C | 129 °F | Roll 2 Temperature | |
| 63.0 °C | 145 °F | Roll 3 Temperature | |
| 210 °C | 410 °F | Cylinder 4 Temperature | |
| 245 °C | 473 °F | Cylinder 2 and Cylinder 3 Temperature | |
| 245 °C | 473 °F | Screen, Me1t Pump, and Connection Temperature | |
| Feed Temperature | 240 °C | 464 °F | |
| Nozzle Temperature | 245 °C | 473 °F | |
| Zone 1 | 180 °C | 356 °F | Barrel Temp of Main Extruder |
| 195 °C | 383 °F | Extrusion Blow Molding | |
| Zone 2 | 210 °C | 410 °F | Extrusion Blow Molding |
| 245 °C | 473 °F | Barrel Temp of Main Extruder | |
| Zone 3 | 210 °C | 410 °F | Extrusion Blow Molding |
| 265 °C | 509 °F | Barrel Temp of Main Extruder | |
| Zone 4 | 210 °C | 410 °F | Extrusion Blow Molding |
| 260 °C | 500 °F | Barrel Temp of Main Extruder | |
| Zone 5 | 240 °C | 464 °F | Barrel Temp of Main Extruder |
| Adapter Temperature | 200 °C | 392 °F | Extrusion Blow Molding |
| 245 °C | 473 °F | ||
| Die Temperature | 195 °C | 383 °F | Extrusion Blow Molding (Die Tip) |
| 247 °C | 477 °F | Die Zone 1 | |
| 249 °C | 480 °F | Die Zone 2 | |
| Head Temperature | 185 °C | 365 °F | Extrusion Blow Molding |
| Mold Temperature | 12.0 - 20.0 °C | 53.6 - 68.0 °F | Extrusion Blow Molding |
| 40.0 °C | 104 °F | ||
| 40.0 - 70.0 °C | 104 - 158 °F | For Thermoforming (Forming time = 3-10 sec) | |
| Drying Temperature | 65.0 °C | 149 °F | |
| Dry Time | 6 - 12 hour | 6 - 12 hour | |
| Injection Pressure | 5.50 MPa | 798 psi | 1st Pressure |
| Hold Pressure | 4.00 MPa | 580 psi | |
| 8.30 MPa | 1200 psi | Extrusion Melt Pressure | |
| Back Pressure | 0.500 MPa | 72.5 psi | |
| Cycle Time - Injection | 2.0 sec | 2.0 sec | |
| 15 sec | 15 sec | 2nd Pressure Time | |
| Cycle Time - Cooling | 15 sec | 15 sec | |