- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.7
- 断裂伸长率 [%]: 88.0
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 4.70
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 3.7 % | 3.7 % | ASTM D638 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 4.70 GPa | 682 ksi | ASTM D790 |
| Compressive Yield Strength | 59.0 MPa | 8560 psi | ASTM D695 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 15 | 15 | ASTM D1044 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 24.0 kV/mm @Thickness 2.00 mm | 610 kV/in @Thickness 0.0787 in | ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | 255 V | 255 V | IEC test |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |