- 密度 [g/cm3]: 1.63
- 吸水率 [%]: 0.04
- 缺口冲击强度: 0.747
- 拉伸强度 [MPa]: 124.0
- 弯曲模量 [MPa]: 11.7
- 硬度: 117.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % @Time 86400 sec | 0.040 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm | 0.0030 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm | 1.40 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 59.4 µm/m-°C | 33.0 µin/in-°F | ASTM D696 |
| Melting Point | 254 °C | 489 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |