- 密度 [g/cm3]: 1.67
- 缺口冲击强度: 11.0
- 弯曲模量 [MPa]: 10.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183-87 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-93 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-93 |
| Flexural Strength | 175 MPa | 25400 psi | ISO 178-93 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 250 °C | 482 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-93 |
| Flammability, UL94 | V-0 @Thickness 0.790 mm | V-0 @Thickness 0.0311 in | |