- 密度 [g/cm3]: 1.19
- 缺口冲击强度: 0.6
- 拉伸强度 [MPa]: 46.0
- 断裂伸长率 [%]: 67.0
- 弯曲模量 [MPa]: 1.75
- 硬度: 105.0
- 热变形温度 [℃]: 73.0
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0060 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
| 53.0 MPa | 7690 psi | ASTM D638 | |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ASTM D638 |
| 47.0 MPa | 6820 psi | ISO 527 | |
| Elongation at Break | 210 % | 210 % | ISO 527 |
| 310 % | 310 % | ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| 5.0 % | 5.0 % | ASTM D638 | |
| Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | ASTM D790 |
| Flexural Modulus | 1.75 GPa | 254 ksi | ISO 178 |
| 1.90 GPa | 276 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.600 J/cm @Temperature -40.0 °C | 1.12 ft-lb/in @Temperature -40.0 °F | ASTM D256 |
| 3.70 J/cm @Temperature 23.0 °C | 6.93 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D4812 | |
| Izod Impact, Notched (ISO) | 6.30 kJ/m² @Temperature -40.0 °C | 3.00 ft-lb/in² @Temperature -40.0 °F | ISO 180 |
| 29.6 kJ/m² @Temperature 23.0 °C | 14.1 ft-lb/in² @Temperature 73.4 °F | ISO 180 | |
| Puncture Energy | 45.0 J | 33.2 ft-lb | Puncture Resistance @Max Load, 23°C; ASTM D3763 |
| 48.0 J | 35.4 ft-lb | Puncture Resistance @Max Load, -40°C; ASTM D3763 | |
| 55.0 J | 40.6 ft-lb | Puncture Resistance @ max load, -40°C; ISO 6603-2 | |
| 71.0 J | 52.4 ft-lb | Puncture Resistance @ max load, 23°C; ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ISO 75 |
| 73.0 °C | 163 °F | ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| 66.0 °C | 151 °F | ISO 75 | |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Optical Properties | Metric | English | Comments |
| Haze | 0.30 % | 0.30 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | Regular Transmittance; ASTM D1003 |
| 91 % | 91 % | Total Transmittance; ASTM D1003 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |
| Mold Temperature | 15.0 - 30.0 °C | 59.0 - 86.0 °F | |
| Drying Temperature | 70.0 °C | 158 °F | |
| Dry Time | 3 hour | 3 hour | |