- 密度 [g/cm3]: 1.56
- 弯曲模量 [MPa]: 9.40
- 热变形温度 [℃]: 226.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 | ||
| Filler Content | 30 % | 30 % | |||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.00 mm | 0.0020 in/in @Thickness 0.118 in | Mold 80°C; ISO 294-4 | ||
| 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Mold 80°C; ISO 294-4 | |||
| 0.0030 cm/cm @Thickness 4.00 mm | 0.0030 in/in @Thickness 0.157 in | Mold 80°C; ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.00 mm | 0.0070 in/in @Thickness 0.118 in | Mold 80°C; ISO 294-4 | ||
| 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | Mold 80°C; ISO 294-4 | |||
| 0.0090 cm/cm @Thickness 4.00 mm | 0.0090 in/in @Thickness 0.157 in | Mold 80°C; ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 142 MPa @Temperature 23.0 °C | 20600 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.0 % @Temperature 23.0 °C | 2.0 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 10.6 GPa @Temperature 23.0 °C | 1540 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 215 MPa @Temperature 23.0 °C | 31200 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 9.40 GPa @Temperature 23.0 °C | 1360 ksi @Temperature 73.4 °F | ISO 178 | ||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+16 ohm-cm @Temperature 23.0 °C | 2.00e+16 ohm-cm @Temperature 73.4 °F | IEC 60093 | ||
| Surface Resistance | 3.00e+14 ohm @Temperature 23.0 °C | 3.00e+14 ohm @Temperature 73.4 °F | IEC 60093 | ||
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.1 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 | ||
| 4.3 @Frequency 100 Hz, Temperature 23.0 °C | 4.3 @Frequency 100 Hz, Temperature 73.4 °F | IEC 60250 | |||
| 4.3 @Frequency 1000 Hz, Temperature 23.0 °C | 4.3 @Frequency 1000 Hz, Temperature 73.4 °F | IEC 60250 | |||
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm, Temperature 90.0 °C | 559 kV/in @Thickness 0.0787 in, Temperature 194 °F | IEC 60243-1 | ||
| 24.0 kV/mm @Thickness 2.00 mm, Temperature 23.0 °C | 610 kV/in @Thickness 0.0787 in, Temperature 73.4 °F | IEC 60243-1 | |||
| 30.0 kV/mm @Thickness 1.00 mm, Temperature 90.0 °C | 762 kV/in @Thickness 0.0394 in, Temperature 194 °F | IEC 60243-1 | |||
| 32.0 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C | 813 kV/in @Thickness 0.0394 in, Temperature 73.4 °F | IEC 60243-1 | |||
| Dissipation Factor | 0.0015 @Frequency 100 Hz, Temperature 23.0 °C | 0.0015 @Frequency 100 Hz, Temperature 73.4 °F | IEC 60250 | ||
| 0.0027 @Frequency 1000 Hz, Temperature 23.0 °C | 0.0027 @Frequency 1000 Hz, Temperature 73.4 °F | IEC 60250 | |||
| 0.0155 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.0155 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 | |||
| Comparative Tracking Index | 350 V @Temperature 23.0 °C | 350 V @Temperature 73.4 °F | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL94 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | UL94 | |||
| Oxygen Index | 21 % | 21 % | ISO 4589-1/-2 | ||
| Glow Wire Test | 650 °C @Thickness 1.50 mm | 1200 °F @Thickness 0.0591 in | IEC 60695-2-12 | ||
| 675 °C @Thickness 1.50 mm | 1250 °F @Thickness 0.0591 in | Ignition; IEC 60695-2-13 | |||
| 700 °C @Thickness 0.800 mm | 1290 °F @Thickness 0.0315 in | IEC 60695-2-12 | |||
| 725 °C @Thickness 0.800 mm | 1340 °F @Thickness 0.0315 in | Ignition; IEC 60695-2-13 | |||
| 775 °C @Thickness 3.00 mm | 1430 °F @Thickness 0.118 in | IEC 60695-2-12 | |||
| 800 °C @Thickness 3.00 mm | 1470 °F @Thickness 0.118 in | Ignition; IEC 60695-2-13 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 227 °C | 441 °F | 10°C/min; ISO 11357-1/-3 | ||
| 260 °C | 500 °F | Optimum | |||
| 250 - 270 °C | 482 - 518 °F | ||||
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | |||
| 100 °C | 212 °F | optimum | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Additive | Lubricant | ||||
| Appearance | Black Color | ||||
| Features | Chemical Resistance, Good | ||||
| Dimensional Stability, Good | |||||
| Gloss, High | |||||
| Moisture Absorption, Low | |||||
| Renewable Resource Content | |||||
| Stiffness, Good | |||||
| Strength, Good | |||||
| Warpage, Low | |||||
| Filler | Glass Fiber Reinforcement | ||||
| Forms | Pellets | ||||
| Generic | PTT | ||||
| Material Status | Commercial | ||||
| Part Marking Code | >PTT-GF30< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PTT | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Glass Reinforced Resins | ||||
| Renewably Sourced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PTT-GF30 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Automotive Applications | ||||
| Consumer Applications | |||||
| General Purpose | |||||
| Industrial Applications | |||||
| Parts, Engineering | |||||
| Parts, Machine/Mechanical | |||||
| Structural Parts | |||||