- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D-1505 | ||
| Melt Index of Compound | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 500 % | 500 % | Blown Film at 1 mil; ASTM D-882 | ||
| Film Elongation at Break, TD | 660 % | 660 % | Blown Film at 1 mil; ASTM D-882 | ||
| Coefficient of Friction | 1.0 | 1.0 | Blown Film at 1 mil; ASTM D-1894 | ||
| Elmendorf Tear Strength, MD | 15.7 g/micron | 400 g/mil | Blown Film at 1 mil; ASTM D-1922 | ||
| Elmendorf Tear Strength, TD | 23.6 g/micron | 600 g/mil | Blown Film at 1 mil; ASTM D-1922 | ||
| Dart Drop | 17.7 g/micron | 450 g/mil | Blown Film at 1 mil; ASTM D-1709 | ||
| Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | Blown Film at 1 mil; ASTM D-882 | ||
| Film Tensile Strength at Break, TD | 36.0 MPa | 5220 psi | Blown Film at 1 mil; ASTM D-882 | ||
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | Blown Film at 1 mil; ASTM D-882 | ||
| 1% Secant Modulus, TD | 214 MPa | 31000 psi | Blown Film at 1 mil; ASTM D-882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Slip | 0.00 | 0.00 | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 14 % | 14 % | Blown Film at 1 mil; ASTM D-1003 | ||
| Gloss | 80 % | 80 % | 60°, Blown Film at 1 mil; ASTM D-2457 | ||
| Descriptive Properties | |||||
| Process Aid | Yes | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.