- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 15.0 MPa | 2180 psi | 2 in per min; ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.0 MPa | 1890 psi | 2 in per min; ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | 2 in per min; ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | 2 in per min; ASTM D882 |
| Elmendorf Tear Strength MD | 95 g | 95 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 450 g | 450 g | ASTM D1922 |
| Dart drop Test | 350 g | 0.772 lb | 26 in; ASTM D1709 |
| Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | 2 in per min; ASTM D882 |
| Film Tensile Strength at Break, TD | 43.0 MPa | 6240 psi | 2 in per min; ASTM D882 |