- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Secant Modulus, MD | 0.130 GPa | 18.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.130 GPa | 18.9 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 50.0 MPa | 7250 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ASTM D2457 |
| Gloss | 90 % | 90 % | at 45°. ASTM D 2457 |
| 150 % | 150 % | at 60°. ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 °C | 518 °F | |