- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 560 % | 560 % | ASTM D882 |
| Film Elongation at Break, TD | 770 % | 770 % | ASTM D882 |
| Secant Modulus, MD | 0.250 GPa | 36.3 ksi | ASTM D882 |
| Secant Modulus, TD | 0.310 GPa | 45.0 ksi | ASTM D882 |
| Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 16.5 g/micron | 420 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 33.1 g/micron | 840 g/mil | ASTM D1922 |
| Dart Drop | 4.70 g/micron | 119 g/mil | F50; 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 53.0 MPa | 7690 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 53.0 MPa | 7690 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D2457 |
| Gloss | 60 % | 60 % | at 45°. ASTM D 2457 |
| 100 % | 100 % | at 60°. ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 °C | 428 °F | |