- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D4883 |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Coefficient of Friction | 2.0 | 2.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 19.7 g/micron | 500 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 27.2 g/micron | 690 g/mil | ASTM D1922 |
| Dart Drop | 20.4 g/micron | 518 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 650 g | 1.43 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 55.9 MPa | 8110 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 45.1 MPa | 6540 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.2 % | 8.2 % | ASTM D2457 |
| Gloss | 69 % | 69 % | 45°. ASTM D 2457 |
| 110 % | 110 % | 60°, ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 232 °C | 450 °F | |