- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D4883 |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 770 % | 770 % | ASTM D882 |
| Secant Modulus, MD | 0.170 GPa | 24.7 ksi | ASTM D882 |
| Secant Modulus, TD | 0.190 GPa | 27.6 ksi | ASTM D882 |
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 19.3 g/micron | 490 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 29.1 g/micron | 740 g/mil | ASTM D1922 |
| Dart Drop | 20.4 g/micron | 518 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 650 g | 1.43 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 46.1 MPa | 6690 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.3 MPa | 5120 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 20 % | 20 % | ASTM D2457 |
| Gloss | 41 % | 41 % | 45°. ASTM D 2457 |
| 65 % | 65 % | 60°. ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 232 °C | 450 °F | |