- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.926
- 拉伸强度 [MPa]: 14.5
- 弯曲强度 [MPa]: 24.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg | 2.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.8. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 24.1 MPa | 3500 psi | Molded property |
| Film Tensile Strength at Yield, MD | 11.7 MPa | 1700 psi | |
| Film Tensile Strength at Yield, TD | 11.7 MPa | 1700 psi | |
| Tensile Strength, Yield | 14.5 MPa | 2100 psi | Molded property |
| Film Elongation at Break, MD | 500 % | 500 % | |
| Film Elongation at Break, TD | 790 % | 790 % | |
| Elongation at Break | 800 % | 800 % | Molded value |
| Coefficient of Friction | 0.60 | 0.60 | |
| Elmendorf Tear Strength MD | 270 g | 270 g | |
| Elmendorf Tear Strength TD | 425 g | 425 g | |
| Elmendorf Tear Strength, MD | 9.00 g/micron | 229 g/mil | |
| Elmendorf Tear Strength, TD | 14.2 g/micron | 361 g/mil | |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | |
| Film Tensile Strength at Break, MD | 62.1 MPa | 9010 psi | |
| Film Tensile Strength at Break, TD | 37.9 MPa | 5500 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 1.2 % | 1.2 % | |
| Gloss | 90 % | 90 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 204 °C | 399 °F | Film extrusion temperature |