- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.92
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D4883 | ||
| Thickness | 25.0 microns | 0.984 mil | |||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 | ||
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 | ||
| Secant Modulus, MD | 0.234 GPa | 33.9 ksi | 1% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.276 GPa | 40.0 ksi | 1% Secant; ASTM D882 | ||
| Elmendorf Tear Strength MD | 200 g | 200 g | |||
| Elmendorf Tear Strength TD | 600 g | 600 g | |||
| Elmendorf Tear Strength, MD | 8.00 g/micron | 203 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 24.0 g/micron | 610 g/mil | ASTM D1922 | ||
| Dart Drop | 6.40 g/micron | 163 g/mil | ASTM D1709A | ||
| Film Tensile Strength at Break, MD | 41.0 MPa | 5950 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 102 °C | 216 °F | 200 g/in seal strength is achieved | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.5 % | 7.5 % | ASTM D1003 | ||
| Gloss | 70 % | 70 % | at 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Process | Film | ||||
| region | US & Canada | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.