- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 |
| Secant Modulus, MD | 0.170 GPa | 24.7 ksi | ASTM D882 |
| Secant Modulus, TD | 0.190 GPa | 27.6 ksi | ASTM D882 |
| Coefficient of Friction | <= 0.20 | <= 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 11.8 g/micron | 300 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 25.5 g/micron | 648 g/mil | ASTM D1922 |
| Dart Drop | 7.00 g/micron | 178 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 37.0 MPa | 5370 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 19 % @Thickness 0.0250 mm | 19 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 37 % | 37 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 195 - 220 °C | 383 - 428 °F | |