- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 38.1 microns | 1.50 mil | 2:1 BUR | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 750 % | 750 % | ASTM D882 | ||
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 | ||
| Coefficient of Friction | <= 0.20 | <= 0.20 | ASTM D1894 | ||
| Elmendorf Tear Strength MD | 170 g | 170 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 400 g | 400 g | ASTM D1922 | ||
| Dart drop Test | 120 g | 0.265 lb | F50; ASTM D1709A | ||
| Film Tensile Strength at Break, MD | 33.8 MPa | 4900 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 24.8 MPa | 3600 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 221 MPa | 32000 psi | ASTM D638 | ||
| 1% Secant Modulus, TD | 248 MPa | 36000 psi | ASTM D638 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12 % | 12 % | ASTM D1003 | ||
| Gloss | 60 % | 60 % | ASTM D523 | ||
| Descriptive Properties | |||||
| Antiblock | Medium | ||||
| Slip | Medium | ||||