- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.9205
- 弯曲模量 [MPa]: 0.276
- 热变形温度 [℃]: 48.0
- 脆化温度 [℃]: -42.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9205 g/cc | 0.03326 lb/in³ | ASTM D1505 |
| ESCR, Bottle | >= 1000 hour | >= 1000 hour | ASTM D2561 |
| Melt Flow | 0.75 g/10 min | 0.75 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 51 | 51 | ASTM D2240 |
| Tensile Strength at Break | 15.0 MPa | 2170 psi | Type IV Specimen; ASTM D638 |
| Elongation at Break | >= 700 % | >= 700 % | Type IV Specimen; ASTM D638 |
| Flexural Modulus | 0.276 GPa | 40.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 |
| Brittleness Temperature | <= -42.0 °C | <= -43.6 °F | F50, Injection molded specimen; ASTM D746 |