- 熔体流动速率 [g/10min]: 50.0
- 密度 [g/cm3]: 0.926
- 拉伸强度 [MPa]: 15.2
- 热变形温度 [℃]: 47.2
- 脆化温度 [℃]: -72.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Melt Flow | 50.0 g/10 min | 50.0 g/10 min | ASTM D1238 |
| Spiral Flow | 45.5 cm | 17.9 in | Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60.0 | 60.0 | ASTM D2240 |
| Tensile Strength at Break | 8.96 MPa | 1300 psi | 20 in/min; ASTM D638 |
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | 20 in/min; ASTM D638 |
| Elongation at Yield | 11.0 % | 11.0 % | 20 in/min; ASTM D638 |
| 1% Secant Modulus | 483 MPa | 70000 psi | 0.5 in/min; ASTM D790 |
| 2% Secant Modulus | 0.421 GPa | 61.0 ksi | 0.5 in/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 47.2 °C | 117 °F | ASTM D648 |
| Vicat Softening Point | 84.4 °C | 184 °F | ASTM D1525 |
| Brittleness Temperature | -72.2 °C | -98.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 191 °C | 375 °F | |
| Front Barrel Temperature | 204 °C | 400 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |
| Compliance Properties | Metric | English | Comments |
| FDA | Yes | Yes | |