- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D1505 | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 | ||
| Antiblock Level | 8000 ppm | 8000 ppm | |||
| Slip Level | 850 ppm | 850 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.3 MPa | 1500 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1500 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 565 % | 565 % | ASTM D882 | ||
| Film Elongation at Break, TD | 775 % | 775 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 16.9 g/micron | 430 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 29.5 g/micron | 750 g/mil | ASTM D1922 | ||
| Dart Drop | 18.9 g/micron | 480 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 55.2 MPa | 8000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 193 MPa | 28000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 207 MPa | 30000 psi | ASTM D882 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||