- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 660 % | 660 % | ASTM D882 |
| Film Elongation at Break, TD | 870 % | 870 % | ASTM D882 |
| Secant Modulus, MD | 0.406 GPa | 58.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.520 GPa | 75.4 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 420 g | 420 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 490 g | 490 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 16.5 g/micron | 420 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 19.3 g/micron | 490 g/mil | ASTM D1922 |
| Dart Drop | 1.57 g/micron | 40.0 g/mil | ASTM D1709 |
| Dart drop Test | 40.0 g | 0.0882 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 26.0 MPa | 3770 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.7 % | 2.7 % | ASTM D1003 |
| Gloss | 90 % | 90 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |