- 熔体流动速率 [g/10min]: 22.0
- 密度 [g/cm3]: 0.918
- 弯曲模量 [MPa]: 0.500
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 - 0.922 g/cc | 0.0332 - 0.0333 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 22 - 28 g/10 min @Load 2.16 kg, Temperature 190 °C | 22 - 28 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1283/L |
| 660 - 840 g/10 min @Load 21.6 kg, Temperature 190 °C | 660 - 840 g/10 min @Load 47.6 lb, Temperature 374 °F | Flow@21.6kg/Flow@2.16kg ratio < 30; ASTM D1283 | |
| Mechanical Properties | Metric | English | Comments |
| Flexural Modulus | >= 0.500 GPa | >= 72.5 ksi | ASTM D1238 |
| Izod Impact, Notched | >= NB @Temperature 23.0 °C | >= NB @Temperature 73.4 °F | ASTM D256 |