- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D 792 | ||
| Thickness | 75.0 microns | 2.95 mil | As tested for properties on this data sheet | ||
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D 882 | ||
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D 882 | ||
| Film Elongation at Break, MD | 760 % | 760 % | ASTM D 882 | ||
| Film Elongation at Break, TD | 705 % | 705 % | ASTM D 882 | ||
| Elmendorf Tear Strength MD | 1206 g | 1206 g | ASTM D 1922 | ||
| Elmendorf Tear Strength TD | 1350 g | 1350 g | ASTM D 1922 | ||
| Elmendorf Tear Strength, MD | 16.1 g/micron | 409 g/mil | ASTM D 1922 | ||
| Elmendorf Tear Strength, TD | 18.0 g/micron | 457 g/mil | ASTM D 1922 | ||
| Dart Drop | 12.1 g/micron | 307 g/mil | ASTM D 1709/A | ||
| Dart drop Test | 909 g | 2.00 lb | F50; ASTM D 1709/A | ||
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D 882 | ||
| Film Tensile Strength at Break, TD | 46.0 MPa | 6670 psi | ASTM D 882 | ||
| 1% Secant Modulus, MD | 182 MPa | 26400 psi | ASTM D 882 | ||
| 1% Secant Modulus, TD | 201 MPa | 29200 psi | ASTM D 882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 22 % | 22 % | ASTM D 1003 | ||
| Gloss | 44 % | 44 % | At 45°; ASTM D 2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Recommended | ||
| Descriptive Properties | |||||
| Low Friction Puncture | 44 (J/mm) | NOVA Chemicals test method | |||