NOVA Chemicals SURPASS FPs016-C Octene sLLDPE Film Resin

NOVA Chemicals SURPASS FPs016-C Octene sLLDPE Film Resin 物性表: NOVA Chemicals SURPASS FPs016-C Octene sLLDPE Film Resin物性表及特性介绍,NOVA Chemicals SURPASS FPs016-C Octene sLLDPE Film Resin注塑参数详情,如需NOVA Chemicals SURPASS FPs016-C Octene sLLDPE Film Resin下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 0.65
  • 密度 [g/cm3]: 0.916
 
Physical PropertiesMetricEnglishComments
Density 0.916 g/cc0.0331 lb/in³ASTM D 792
Thickness 25.0 microns0.984 milAs tested for properties on this data sheet
 12.7 - 127 microns0.500 - 5.00 milRecommended range for processing
Melt Flow 0.65 g/10 min
@Load 2.16 kg,
Temperature 190 °C
0.65 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, MD 8.50 MPa1230 psiASTM D 882
Film Tensile Strength at Yield, TD 8.50 MPa1230 psiASTM D 882
Film Elongation at Break, MD 470 %470 %ASTM D 882
Film Elongation at Break, TD 780 %780 %ASTM D 882
Elmendorf Tear Strength MD 350 g350 gASTM D 1922
Elmendorf Tear Strength TD 430 g430 gASTM D 1922
Elmendorf Tear Strength, MD 14.0 g/micron356 g/milASTM D 1922
Elmendorf Tear Strength, TD 17.2 g/micron437 g/milASTM D 1922
Dart Drop 28.0 g/micron711 g/milASTM D 1709/A
Dart drop Test 700 g1.54 lbF50; ASTM D 1709/A
Film Tensile Strength at Break, MD 47.0 MPa6820 psiASTM D 882
Film Tensile Strength at Break, TD 44.0 MPa6380 psiASTM D 882
1% Secant Modulus, MD 126 MPa18300 psiASTM D 882
1% Secant Modulus, TD 138 MPa20000 psiASTM D 882
Heat Seal Strength Initiation Temperature 100 °C212 °FTemperature at which a 2-mil film achieves a seal strength of 4.4N/13mm. Tested at 0.5s dwell, 0.27 N/mm² bar pressure, 305mm/min. pull speed.
 
Optical PropertiesMetricEnglishComments
Haze 7.0 %7.0 %LDPE blended; ASTM D 1003
 15 %15 %100% LLDPE; ASTM D 1003
Gloss 38 %38 %At 45°, 100% LLDPE; ASTM D 2457
 72 %72 %At 45°, LDPE blended; ASTM D 2457
 
Processing PropertiesMetricEnglishComments
Melt Temperature 185 - 220 °C365 - 428 °FRecommended
Die Opening 0.0889 - 0.216 cm0.0350 - 0.0850 inRecommended range
Blow-up Ratio (BUR) 2.0 - 3.52.0 - 3.5Optimum range
 
Descriptive Properties
Low Friction Puncture98 (J/mm)NOVA Chemicals test method

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-40634.html

免责声明: 本文 NOVA Chemicals SURPASS FPs016-C Octene sLLDPE Film Resin 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4