- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg | 0.90 g/10 min @Load 4.76 lb | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.5 MPa | 1810 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Coefficient of Friction, Dynamic | 0.12 | 0.12 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 | 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 13.8 g/micron | 351 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 27.6 g/micron | 701 g/mil | ASTM D1922 |
| Dart Drop | 7.00 g/micron | 178 g/mil | F50,38mm dart 66mm height; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Gloss | 80 % | 80 % | 60; ASTM D523 |