- 熔体流动速率 [g/10min]: 0.65
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 11.8
- 弯曲模量 [MPa]: 0.400
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ISO 1872/1 |
| ESCR, Bottle | 250 hour @Temperature 50.0 °C | 250 hour @Temperature 122 °F | BP 13C/25 |
| Melt Flow | 0.65 g/10 min @Load 2.16 kg | 0.65 g/10 min @Load 4.76 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 11.8 MPa | 1710 psi | BP 13B/1 |
| Elongation at Break | 1000 % | 1000 % | BP 13B/1 |
| Flexural Modulus | 0.400 GPa | 58.0 ksi | ISO 178-1975 |