- 拉伸强度 [MPa]: 13.7
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 4.0 hour @Thickness 3.80 mm, Temperature 50.0 °C | 4.0 hour @Thickness 0.150 in, Temperature 122 °F | non slit; ASTM D1693 |
| Base Resin Melt Index | 50 g/10 min | 50 g/10 min | I2; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 13.7 MPa | 1990 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| 1% Secant Modulus | 343.23 MPa | 49782 psi | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 88.0 °C | 190 °F | resin; ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 220 °C | 338 - 428 °F | |
| Mold Temperature | 10.0 - 40.0 °C | 50.0 - 104 °F | |