- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D-1505 | ||
| Thickness | 50.0 - 200 microns | 1.97 - 7.87 mil | |||
| Melt Flow | 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.25 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 24.1 MPa | 3500 psi | 10 in/min; ASTM D-882 | ||
| Film Tensile Strength at Yield, TD | 20.7 MPa | 3000 psi | 10 in/min; ASTM D-882 | ||
| Film Elongation at Break, MD | 350 % | 350 % | 10 in/min; ASTM D-882 | ||
| Film Elongation at Break, TD | 600 % | 600 % | 10 in/min; ASTM D-882 | ||
| Secant Modulus, MD | 0.159 GPa | 23.1 ksi | 0.1 mm/mm-min Initial Strain Rate; ASTM D-882 | ||
| Secant Modulus, TD | 0.179 GPa | 26.0 ksi | 0.1 mm/mm-min Initial Strain Rate; ASTM D-882 | ||
| Dart Drop | 8.46 g/micron | 215 g/mil | ASTM D-1709; F50 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | Europe/Turkey | ||||
| International | |||||
| Mexico | |||||
| US & Canada | |||||