- 熔体流动速率 [g/10min]: 70.0
- 密度 [g/cm3]: 0.914
- 弯曲模量 [MPa]: 0.130
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.914 g/cc | 0.0330 lb/in³ | AT Plastics PTM-03 |
| Melt Flow | 70 g/10 min @Load 0.325 kg, Temperature 125 °C | 70 g/10 min @Load 0.716 lb, Temperature 257 °F | Modified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Tensile Strength at Break | 8.00 MPa | 1160 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 120 % | 120 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.130 GPa | 18.9 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 102 °C | 216 °F | DSC; ASTM D3417 |
| Ring & Ball Softening Point | 117 °C | 243 °F | ASTM E28 |