- 熔体流动速率 [g/10min]: 1.4
- 密度 [g/cm3]: 0.929
- 弯曲强度 [MPa]: 2.8
- 脆化温度 [℃]: -79.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | AT Plastics PTM-03 |
| Carbon Black Loading | 2.2 % | 2.2 % | Deviation from Target; ASTM D1603 |
| Melt Flow | 1.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | Type IV (50 mm/min); ASTM D638 |
| Tensile Strength, Ultimate | 2.80 MPa | 406 psi | Certified Design Strength; CSA B137 |
| Elongation at Break | 530 % | 530 % | Type IV (50 mm/min); ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 113 °C | 235 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Brittleness Temperature | -79.0 °C | -110 °F | ASTM D746 |