- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183-A |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 230 % | 230 % | ISO 1184 |
| Film Elongation at Break, TD | 500 % | 500 % | ISO 1184 |
| Elmendorf Tear Strength MD | 600 g | 600 g | ISO 6283-2 |
| Elmendorf Tear Strength TD | 250 g | 250 g | ISO 6283-2 |
| Elmendorf Tear Strength, MD | 12.0 g/micron | 305 g/mil | ISO 6283-2 |
| Elmendorf Tear Strength, TD | 5.00 g/micron | 127 g/mil | ISO 6283-2 |
| Dart Drop | 2.50 g/micron | 63.5 g/mil | F50; ISO 7765-A |
| Dart drop Test | 125 g | 0.276 lb | F50; ISO 7765-A |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 1184 |
| Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ISO 1184 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 65 % | 65 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 °C | 320 °F | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |