- 熔体流动速率 [g/10min]: 24.5
- 密度 [g/cm3]: 0.925
- 拉伸强度 [MPa]: 11.0
- 弯曲强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.186
- 脆化温度 [℃]: -48.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Melt Flow | 24.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 24.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 54 | 54 | ASTM D2240 |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Flexural Modulus | 0.186 GPa | 27.0 ksi | 3 pt. secant; ASTM D790 |
| 0.269 GPa | 39.0 ksi | 3 pt. Tangent; ASTM D790 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Brittleness Temperature | -48.0 °C | -54.4 °F | ASTM D746 |