- 熔体流动速率 [g/10min]: 21.0
- 密度 [g/cm3]: 0.917
- 拉伸强度 [MPa]: 7.7
- 弯曲强度 [MPa]: 11.2
- 弯曲模量 [MPa]: 0.124
- 脆化温度 [℃]: -72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 190 °C | 21 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Ultimate | 11.2 MPa | 1620 psi | ASTM D638 |
| Tensile Strength, Yield | 7.70 MPa | 1120 psi | ASTM D638 |
| Elongation at Break | 540 % | 540 % | ASTM D638 |
| Flexural Modulus | 0.124 GPa | 18.0 ksi | 3 pt. secant; ASTM D790 |
| 0.159 GPa | 23.1 ksi | 3 pt. Tangent; ASTM D790 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 87.0 °C | 189 °F | ASTM D1525 |
| Brittleness Temperature | <= -72.0 °C | <= -97.6 °F | ASTM D746 |