- 熔体流动速率 [g/10min]: 16.0
- 密度 [g/cm3]: 0.917
- 拉伸强度 [MPa]: 11.0
- 弯曲强度 [MPa]: 9.7
- 弯曲模量 [MPa]: 0.207
- 脆化温度 [℃]: -48.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D1505 |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 190 °C | 16 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | ASTM D2240 |
| Tensile Strength, Ultimate | 9.70 MPa | 1410 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 320 % | 320 % | ASTM D638 |
| Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant; ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 89.0 °C | 192 °F | ASTM D1525 |
| Brittleness Temperature | -48.0 °C | -54.4 °F | ASTM D746 |