- 密度 [g/cm3]: 0.921
- 拉伸强度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 - 0.923 g/cc | 0.0333 - 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 0.23 - 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.23 - 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 625 % | 625 % | ASTM D882 |
| Elongation at Break | 585 % | 585 % | ASTM D638 |
| Secant Modulus, MD | 0.115 GPa | 16.7 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.125 GPa | 18.1 ksi | 5%; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.45 | 0.45 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 6.00 g/micron | 152 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.60 g/micron | 117 g/mil | ASTM D1922 |
| Dart drop Test | 190 g | 0.419 lb | (method A); ASTM D1709 |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.5 MPa | 3410 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 180 °C | 338 - 356 °F | Plasticizing Zone |
| 180 - 190 °C | 356 - 374 °F | Mixture Zone | |
| Feed Temperature | 160 - 175 °C | 320 - 347 °F | |
| Adapter Temperature | 185 - 205 °C | 365 - 401 °F | |
| Blow-up Ratio (BUR) | 3.0 | 3.0 | Recommended |