- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.912
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.912 g/cc | 0.0329 lb/in³ | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg | 5.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 68.3 MPa | 9910 psi | |
| Film Tensile Strength at Yield, TD | 66.9 MPa | 9700 psi | |
| Film Elongation at Break, MD | 605 % | 605 % | |
| Film Elongation at Break, TD | 866 % | 866 % | |
| Elmendorf Tear Strength MD | 296 g | 296 g | Unspecified film thickness |
| Elmendorf Tear Strength TD | 635 g | 635 g | Unspecified film thickness |
| Dart drop Test | 185 g | 0.408 lb | |
| Film Tensile Strength at Break, MD | 51.8 MPa | 7510 psi | |
| Film Tensile Strength at Break, TD | 37.4 MPa | 5420 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 0.60 % | 0.60 % | |
| Gloss | 93 % | 93 % | 45° |