- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.921
- 缺口冲击强度: 69.4
- 拉伸强度 [MPa]: 9.5
- 弯曲强度 [MPa]: 10.8
- 弯曲模量 [MPa]: 0.274
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | |
| Viscosity | 56000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 56000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 99000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 99000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 265000 cP @Shear Rate 300 1/s, Temperature 190 °C | 265000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg | 2.0 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 10.8 MPa | 1570 psi | |
| Tensile Strength, Yield | 9.50 MPa | 1380 psi | |
| Elongation at Break | 240 % | 240 % | |
| Modulus of Elasticity | 0.164 GPa | 23.8 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.274 GPa | 39.7 ksi | |
| Izod Impact, Notched (ISO) | 69.4 kJ/m² @Temperature -50.0 °C | 33.0 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 92.0 °C | 198 °F | |