- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.921
- 拉伸强度 [MPa]: 11.0
- 弯曲强度 [MPa]: 13.8
- 弯曲模量 [MPa]: 0.221
- 脆化温度 [℃]: -73.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D4883 |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | 500 mm/min (20 in./min); ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | 500 mm/min (20 in./min); ASTM D638 |
| Elongation at Break | 500 % | 500 % | 500 mm/min (20 in./min); ASTM D638 |
| Flexural Modulus | 0.221 GPa | 32.1 ksi | 2% Secant; ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Brittleness Temperature | -73.0 °C | -99.4 °F | ASTM D746 |