- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.2 MPa | 1620 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 186 % | 186 % | ASTM D882 |
| Film Elongation at Break, TD | 513 % | 513 % | ASTM D882 |
| Secant Modulus, MD | 0.193 GPa | 28.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.258 GPa | 37.4 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.60 | >= 0.60 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 10.5 g/micron | 267 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.90 g/micron | 99.1 g/mil | ASTM D1922 |
| Dart Drop | 2.40 g/micron | 61.0 g/mil | F50; ASTM D 1709/A |
| Film Tensile Strength at Break, MD | 27.2 MPa | 3950 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.8 MPa | 2580 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.9 % | 9.9 % | ASTM D1003 |
| Gloss | 49.3 % | 49.3 % | at 45°; ASTM D 2457 |