- 熔体流动速率 [g/10min]: 0.27
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.922 g/cc | 0.922 g/cc | ISO 1183 |
| Thickness | 50.0 - 250 microns | 1.97 - 9.84 mil | Recommended |
| Melt Flow | 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.27 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ISO 527-3 |
| Film Elongation at Break, MD | 400 % | 400 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 2.2418 g/micron | 56.942 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 3.5665 g/micron | 90.589 g/mil | ISO 6383-2 |
| Dart drop Test | 330 g | 0.728 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 160 MPa | 23200 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 180 MPa | 26100 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 113 °C | 235 °F | Internal method |
| Vicat Softening Point | 93.0 °C @Load 1.00 kg | 199 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | ISO 14782 |
| Gloss | 50 % | 50 % | 45°; ASTM D2457 |