- 熔体流动速率 [g/10min]: 200.0
- 拉伸强度 [MPa]: 8.0
- 弯曲模量 [MPa]: 0.100
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.915 g/cc | 0.915 g/cc | ISO 1183 |
Melt Flow | 200 g/10 min @Load 2.16 kg, Temperature 190 °C | 200 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 42 | 42 | ISO 868/A |
Tensile Strength, Yield | 8.00 MPa | 1160 psi | ISO 527 |
Flexural Modulus | 0.100 GPa | 14.5 ksi | ISO 178 |
Thermal Properties | Metric | English | Comments |
Melting Point | 102 °C | 216 °F | Internal method |
Vicat Softening Point | 72.0 °C @Load 1.00 kg | 162 °F @Load 2.20 lb | ISO 306/A |
Brittleness Temperature | <= 0.000 °C | <= 32.0 °F | ASTM D746 |